SUPERFIX High-temperature plastics. Physical properties. Mechanical | Thermal | Electrical | Miscellaneous |
||||||||||||||
|
|
|
|
Mechanical
properties |
|||||||||||
|
|
|
|
Densi-ty (DIN 53 479) |
Tensile strength at yield (DIN 53 455) |
Tensile strength at break (DIN 53 455) |
Elonga-tion at break (DIN 53 452) |
Modulus of elasticity after tensile test (DIN 53 457) |
Modulus of elasticity after flexural test (DIN 53 457) |
Ball Indentation hardness (30s, DIN 53 456 |
Impact
resistance (DIN53 453) no.br.=no breaking |
Creep rupture strength after 1000h with static
load |
Time yield limit for 1% elongation after 1000h |
Co-efficient of friction p=0.05N/ mm2 v=0.6m/s on hardened
steel and ground |
Wear (condition as previous) |
|
DIN Abbrevia-tion
|
Additive
And/or colour |
Service
tempe-rature °C long term |
r g/cm3 |
sS MPa |
sR MPa |
eR % |
Et MPa |
EB MPa |
Hk MPa |
an kJ/m2 |
sB/1000 MPa |
s1/1000 MPa |
m - |
TM °C |
|
PVDF |
|
150 |
1,77 |
50 |
|
>50 |
2000 |
2000 |
105 |
no.br. |
34 |
3 |
0,3 |
|
|
ETFE |
|
150 |
1,70 |
40 |
|
40 |
800 |
|
60 |
no.br. |
|
|
0,4 |
|
|
PVDF CF 8 |
8% carbon fibre, black |
150 |
1,78 |
|
93 |
1 |
6000 |
6000 |
|
|
|
|
0,23 |
|
|
PSU |
Translucent |
160 |
1,24 |
70 |
|
>50 |
2400 |
|
140 |
no.br. |
42 |
22 |
0,4 |
|
|
PES |
Translucent |
180 |
1,37 |
90 |
|
30 |
2700 |
|
150 |
|
|
20 |
|
|
|
PEI |
Translucent |
170 |
1,27 |
105 |
|
>50 |
3200 |
3300 |
165 |
no.br. |
|
|
|
|
|
PEI GF 30 |
30% glass fibre |
170 |
1,51 |
|
160 |
3 |
9000 |
9000 |
|
no.br. |
|
|
|
|
|
PPS |
|
230 |
1,35 |
75 |
|
4 |
3500 |
3600 |
190 |
60 |
|
|
|
|
|
PPS GF40 |
40% glass fibre |
230 |
1,64 |
|
185 |
1,5 |
14500 |
13000 |
>300 |
30 |
|
|
|
|
|
PPS |
10% carbon fibre, PTFE, graphite, black |
230 |
1,54 |
|
115 |
1,5 |
10000 |
|
|
20 |
|
|
0,21 |
0,69 |
|
PTFE |
|
260 |
2,18 |
25 |
|
>50 |
700 |
|
30 |
no.br. |
5 |
1,50 |
0,08-0,1 |
21 |
|
PEEK |
Also in black** |
260 |
1,32 |
95 |
|
25 |
3000 |
4100 |
|
no.br. |
|
|
0,3-0,38 |
|
|
PEEK GF 30 |
30% glass fibre |
260 |
1,49 |
|
180 |
25 |
9500 |
10000 |
|
60 |
36 |
|
0,38-0,46 |
|
|
PEEK CF 30 |
30% carbon fibre, black |
260 |
1,44 |
|
210 |
2 |
20000 |
20200 |
|
30 |
|
|
|
|
|
PEEK |
10% carbon fibre, PTFE, graphite, black |
260 |
1,48 |
|
120 |
2 |
9000 |
8100 |
|
|
|
|
0,11 |
|
|
PI CS 15 |
15% graphite, anthracite |
300 |
1,42 |
|
88 |
2,8 |
4000 |
4200 |
|
21 |
|
|
0,28-0,32 |
|
|
PI CS 40 |
40% graphite |
300 |
1,58 |
|
31 |
1,4 |
|
|
80 |
|
|
|
|
|
|
PI FF 30 |
30% PTFE |
300 |
1,51 |
|
82 |
4,1 |
|
|
84 |
|
|
|
|
|
|
PI |
15% graphite, 10% PTFE |
300 |
1,48 |
|
77 |
2,9 |
|
|
85 |
|
|
|
|
|
|
PI |
Polyimid P84, brown |
260 |
1,85 |
|
15 |
200 |
|
|
65 |
no.br. |
|
|
0,15-0,2 |
|
|
**For materials where “also in black”
is detailed under “additives and/or colour” the electrical values do
not apply to the black type. Additionally, the black variants are
resistant to weathering. |
||||||||||||||
|
+ = Resistant (+) = Limited resistance - = Not resistant (depending on concentration, time and
temperature) |
||||||||||||||