Page 1 | Page 2
|
SUPERFIX High-temperature plastics. Physical properties.
Mechanical | Thermal | Electrical | Miscellaneous |
||||||||||||||
|
|
|
|
Mechanical properties |
|||||||||||
|
|
|
|
Density (DIN 53 479) |
Tensile strength at yield
(DIN 53 455) |
Tensile strength at break
(DIN 53 455) |
Elongation
at break (DIN 53 455) |
Modulus of
elasticity after tensile test (DIN 53 457) |
Modulus of elasticity after
flexural test (DIN 53 457) |
Ball Indentation
hardness (30s, DIN 53 456 |
Impact resistance (DIN53 453) no.br.=no
breaking |
Creep
rupture strength after 1000h with static load |
Time yield
limit for 1% elongation after 1000h |
Co-efficient
of friction p=0,05N/mm2
v=0,6m/s on hardened steel and ground |
Wear (conditions as previous) |
DIN
Abbreviation
|
Additives And/or colour |
Service tempe-rature °C long term |
r g/cm3 |
sS MPa |
sR MPa |
eR % |
Et MPa |
EB MPa |
Hk MPa
|
an kJ/m2 |
sB/1000 MPa |
s1/1000 MPa |
m - |
TM °C |
|
PPE |
Grey |
85 |
1,06 |
55 |
|
30 |
2300 |
|
140 |
no.Br. |
|
21 |
0,4 |
90 |
|
PPE GF 30 |
30% glass fibre, beige |
85 |
1,26 |
|
|
2,5 |
9000 |
|
|
35 |
|
47 |
|
|
|
ABS |
Grey |
85 |
1,06 |
50 |
|
10 |
2400 |
|
90 |
no.Br. |
28 |
17 |
0,5 |
8,4 |
|
PP |
Also in Black** |
100 |
0,91 |
|
|
>50 |
1300 |
|
80 |
no.Br. |
22 |
4 |
0,3 |
11 |
|
PE-HD |
Also in Black** |
90 |
0,96 |
|
25 |
>50 |
1000 |
1000-1400 |
45-60 |
no.Br. |
12,5 |
3 |
0,29 |
|
|
POM Copolymer |
Also in Black** |
100 |
1,41 |
65 |
|
30 |
2700 |
|
155 |
no.Br. |
40 |
13 |
0,32 |
8,9 |
|
POM GF 30 Copolymer |
30% glass fibre |
100 |
1,61 |
|
120 |
2 |
8000 |
|
|
30 |
|
40 |
0,5 |
|
|
POM Copolymer |
With lubricant blue |
100 |
1,34 |
45 |
|
10 |
2300 |
2100 |
113 |
30 |
|
|
~0,2 |
|
|
POM Copolymer |
Conductive Carbon black, black |
100 |
1,41 |
50 |
|
15 |
2000 |
|
100 |
50 |
|
|
|
|
|
POM Copolymer |
PTFE |
100 |
1,52 |
45 |
|
15 |
2400 |
|
|
60 |
|
|
0,25 |
|
|
POM Homopolymer |
|
100 |
1,42 |
70 |
|
25 |
3000 |
2620 |
170 |
no.Br. |
40 |
13 |
0,34 |
4,6 |
|
POM Homopolymer |
PTFE, Brown |
100 |
1,54 |
48 |
|
10 |
2900 |
2410 |
|
40 |
|
|
0,14 |
|
|
POM GF 20 Homopolymer |
20% glass fibre |
100 |
1,56 |
|
55 |
10 |
6000 |
|
|
|
|
28 |
0,35 |
|
|
POM Homopolymer |
With lubricant |
100 |
1,42 |
70 |
|
20 |
3100 |
2760 |
|
no.Br. |
|
|
0,1 |
|
|
PA 6 G |
Also in blue |
100 |
1,15 |
60* 85 |
|
3 50* |
1700* 3300 |
|
90-160 |
no.Br. |
50 |
5 |
0,4 |
|
|
PA 6 G |
MoS2, Black |
100 |
1,15 |
75 |
|
40 60* |
2800 |
|
145 |
|
|
|
|
|
|
PA 6-3-T |
transparent |
100 |
1,12 |
90 |
|
>50 |
2800 |
|
100 |
no.Br. |
50 |
12 |
|
|
|
PA 6 |
|
100 |
1,13 |
>50 |
|
70 200* |
1800* 3200 |
|
70-160 |
no.Br. |
45 |
4,5 |
0,38- 0,45 |
0,23 |
|
PA 66 |
Heat stabilizer, brown |
115 |
1,14 |
80 |
|
>50 |
2000 |
|
100-165 |
no.Br. |
|
6 |
|
|
|
PA 66 |
With lubricant |
90 |
1,10 |
60 |
|
10 |
1700 |
|
100-140 |
50 |
|
3 |
0,18-0,2 |
0,08 |
|
PA 66 GF 30 |
30% glass fibre, black |
110 |
1,35 |
|
160 |
3 |
8000 |
|
200-270 |
70 |
|
40 |
0,45-0,5 |
|
|
PA 66 CF 20 |
20% carbon fibre, black |
110 |
1,23 |
|
200 |
2 |
11000 |
|
200-240 |
50 |
|
|
0,16-0,2 |
0,7 |
|
PBT GF 30 |
30% glass fibre |
120 |
1,53 |
|
135 |
2,5 |
10000 |
|
|
60 |
|
57 |
0,24 |
|
|
PET |
|
110 |
1,34 |
55 |
|
>50 |
2500 |
|
145 |
no.Br. |
36 |
13 |
0,25 |
0,35 |
|
PC |
Transparent |
120 |
1,20 |
60 |
|
>50 |
2400 |
|
100 |
no.Br. |
48 |
18 |
0,52-0,58 |
22 |
|
PC GF 30 |
30% glass fibre |
120 |
1,43 |
|
70 |
3 |
5800 |
|
150 |
35 |
>50 |
|
|
|
|
PMP |
Transparent |
120 |
0,83 |
20 |
|
>50 |
750 |
|
|
no.Br. |
|
|
|
|
|
PA 11 |
|
80 |
1,04 |
40 |
|
>50 |
2100 |
|
90 |
no.Br. |
23 |
3,5 |
0,32-0,38 |
0,8 |
|
PA 46 |
|
130 |
1,18 |
100 |
|
40 |
3300 |
|
170-200 |
no.Br. |
|
|
0,2-0,45 |
|
|
Remark: For polyamides the values
strongly depend on the humidity contents. *humid, after storage in standard
atmosphere 23°C 50 RH (DIN 50 014) until saturation. **For materials where “also in black”
is detailed under “additives and/or colour” the electrical values do not
apply to the black type. Additionally, the black variants are resistant to
weathering. |
||||||||||||||
|
+ = Resistant (+) = Limited resistance - = Not resistant (depending on concentration, time and
temperature) |
||||||||||||||